AWS E320 vs. SAE-AISI H43 Steel
Both AWS E320 and SAE-AISI H43 steel are iron alloys. They have 45% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is AWS E320 and the bottom bar is SAE-AISI H43 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 200 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 77 |
| Tensile Strength: Ultimate (UTS), MPa | 620 | |
| 710 to 2140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 270 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1530 |
| Melting Onset (Solidus), °C | 1360 | |
| 1480 |
| Specific Heat Capacity, J/kg-K | 460 | |
| 460 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 38 | |
| 14 |
| Density, g/cm3 | 8.2 | |
| 7.9 |
| Embodied Carbon, kg CO2/kg material | 6.5 | |
| 8.2 |
| Embodied Energy, MJ/kg | 91 | |
| 120 |
| Embodied Water, L/kg | 220 | |
| 100 |
Common Calculations
| PREN (Pitting Resistance) | 28 | |
| 31 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 | |
| 25 to 75 |
| Strength to Weight: Bending, points | 20 | |
| 22 to 46 |
| Thermal Shock Resistance, points | 16 | |
| 21 to 62 |
Alloy Composition
| Carbon (C), % | 0 to 0.070 | |
| 0.5 to 0.65 |
| Chromium (Cr), % | 19 to 21 | |
| 3.8 to 4.5 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 |
| Iron (Fe), % | 31.8 to 43.5 | |
| 83.2 to 85.9 |
| Manganese (Mn), % | 0.5 to 2.5 | |
| 0.15 to 0.4 |
| Molybdenum (Mo), % | 2.0 to 3.0 | |
| 7.8 to 8.5 |
| Nickel (Ni), % | 32 to 36 | |
| 0 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.6 | |
| 0.2 to 0.45 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 1.8 to 2.2 |