AWS E33-31 vs. C71000 Copper-nickel
AWS E33-31 belongs to the iron alloys classification, while C71000 copper-nickel belongs to the copper alloys. They have a modest 23% of their average alloy composition in common, which, by itself, doesn't mean much. There are 19 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is AWS E33-31 and the bottom bar is C71000 copper-nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 130 |
| Poisson's Ratio | 0.27 | |
| 0.33 |
| Shear Modulus, GPa | 81 | |
| 49 |
| Tensile Strength: Ultimate (UTS), MPa | 810 | |
| 320 to 560 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 230 |
| Melting Completion (Liquidus), °C | 1380 | |
| 1200 |
| Melting Onset (Solidus), °C | 1330 | |
| 1150 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 400 |
| Thermal Expansion, µm/m-K | 14 | |
| 15 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 36 | |
| 37 |
| Density, g/cm3 | 7.9 | |
| 8.9 |
| Embodied Carbon, kg CO2/kg material | 6.0 | |
| 4.3 |
| Embodied Energy, MJ/kg | 86 | |
| 63 |
| Embodied Water, L/kg | 260 | |
| 290 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.2 |
| Stiffness to Weight: Bending, points | 25 | |
| 19 |
| Strength to Weight: Axial, points | 28 | |
| 10 to 18 |
| Strength to Weight: Bending, points | 24 | |
| 12 to 17 |
| Thermal Shock Resistance, points | 19 | |
| 12 to 20 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.030 | |
| 0 |
| Chromium (Cr), % | 31 to 35 | |
| 0 |
| Copper (Cu), % | 0.4 to 0.8 | |
| 73.5 to 80.5 |
| Iron (Fe), % | 24.7 to 34.8 | |
| 0.5 to 1.0 |
| Lead (Pb), % | 0 | |
| 0 to 0.050 |
| Manganese (Mn), % | 2.5 to 4.0 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 1.0 to 2.0 | |
| 0 |
| Nickel (Ni), % | 30 to 32 | |
| 19 to 23 |
| Nitrogen (N), % | 0.3 to 0.5 | |
| 0 |
| Phosphorus (P), % | 0 to 0.020 | |
| 0 |
| Silicon (Si), % | 0 to 0.9 | |
| 0 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 1.0 |
| Residuals, % | 0 | |
| 0 to 0.5 |