AWS E383 vs. AISI 317L Stainless Steel

Both AWS E383 and AISI 317L stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is AISI 317L stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 34
44
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
82
Tensile Strength: Ultimate (UTS), MPa 580
550

Thermal Properties

Latent Heat of Fusion, J/g 320
290
Melting Completion (Liquidus), °C 1420
1400
Melting Onset (Solidus), °C 1370
1380
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
14
Thermal Expansion, µm/m-K 14
17

Otherwise Unclassified Properties

Base Metal Price, % relative 37
21
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.4
4.3
Embodied Energy, MJ/kg 89
59
Embodied Water, L/kg 240
160

Common Calculations

PREN (Pitting Resistance) 40
31
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 3.1
3.8
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.030
Chromium (Cr), % 26.5 to 29
18 to 20
Copper (Cu), % 0.6 to 1.5
0
Iron (Fe), % 28.8 to 39.2
58 to 68
Manganese (Mn), % 0.5 to 2.5
0 to 2.0
Molybdenum (Mo), % 3.2 to 4.2
3.0 to 4.0
Nickel (Ni), % 30 to 33
11 to 15
Nitrogen (N), % 0
0 to 0.1
Phosphorus (P), % 0 to 0.020
0 to 0.045
Silicon (Si), % 0 to 0.9
0 to 0.75
Sulfur (S), % 0 to 0.020
0 to 0.030