AWS E383 vs. EN 1.1233 Steel

Both AWS E383 and EN 1.1233 steel are iron alloys. They have a modest 35% of their average alloy composition in common, which, by itself, doesn't mean much. There are 21 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS E383 and the bottom bar is EN 1.1233 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
72
Tensile Strength: Ultimate (UTS), MPa 580
680 to 760

Thermal Properties

Latent Heat of Fusion, J/g 320
250
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
51
Thermal Expansion, µm/m-K 14
12

Otherwise Unclassified Properties

Base Metal Price, % relative 37
1.9
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 6.4
1.4
Embodied Energy, MJ/kg 89
19
Embodied Water, L/kg 240
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 20
24 to 27
Strength to Weight: Bending, points 19
22 to 24
Thermal Diffusivity, mm2/s 3.1
14
Thermal Shock Resistance, points 15
22 to 24

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0.52 to 0.6
Chromium (Cr), % 26.5 to 29
0
Copper (Cu), % 0.6 to 1.5
0 to 0.3
Iron (Fe), % 28.8 to 39.2
98 to 99.1
Manganese (Mn), % 0.5 to 2.5
0.9 to 1.2
Molybdenum (Mo), % 3.2 to 4.2
0
Nickel (Ni), % 30 to 33
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.020
0 to 0.025
Silicon (Si), % 0 to 0.9
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.030