AWS E385 vs. AWS E90C-B9

Both AWS E385 and AWS E90C-B9 are iron alloys. They have 58% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is AWS E90C-B9.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 34
18
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
75
Tensile Strength: Ultimate (UTS), MPa 580
710

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1410
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 14
25
Thermal Expansion, µm/m-K 14
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
6.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
8.0

Otherwise Unclassified Properties

Base Metal Price, % relative 31
7.0
Density, g/cm3 8.1
7.8
Embodied Carbon, kg CO2/kg material 5.8
2.6
Embodied Energy, MJ/kg 79
37
Embodied Water, L/kg 200
91

Common Calculations

PREN (Pitting Resistance) 36
13
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
25
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 3.6
6.9
Thermal Shock Resistance, points 15
20

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0 to 0.030
0.080 to 0.13
Chromium (Cr), % 19.5 to 21.5
8.0 to 10.5
Copper (Cu), % 1.2 to 2.0
0 to 0.2
Iron (Fe), % 41.8 to 50.1
84.4 to 90.9
Manganese (Mn), % 1.0 to 2.5
0 to 1.2
Molybdenum (Mo), % 4.2 to 5.2
0.85 to 1.2
Nickel (Ni), % 24 to 26
0 to 0.8
Niobium (Nb), % 0
0.020 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.9
0 to 0.5
Sulfur (S), % 0 to 0.020
0 to 0.015
Vanadium (V), % 0
0.15 to 0.3
Residuals, % 0
0 to 0.5