AWS E385 vs. EN 1.3541 Stainless Steel

Both AWS E385 and EN 1.3541 stainless steel are iron alloys. They have 60% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is AWS E385 and the bottom bar is EN 1.3541 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
76
Tensile Strength: Ultimate (UTS), MPa 580
710

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1390
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 14
30
Thermal Expansion, µm/m-K 14
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
3.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
3.5

Otherwise Unclassified Properties

Base Metal Price, % relative 31
7.0
Density, g/cm3 8.1
7.7
Embodied Carbon, kg CO2/kg material 5.8
1.9
Embodied Energy, MJ/kg 79
27
Embodied Water, L/kg 200
100

Common Calculations

PREN (Pitting Resistance) 36
14
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 20
26
Strength to Weight: Bending, points 19
23
Thermal Diffusivity, mm2/s 3.6
8.1
Thermal Shock Resistance, points 15
26

Alloy Composition

Carbon (C), % 0 to 0.030
0.43 to 0.5
Chromium (Cr), % 19.5 to 21.5
12.5 to 14.5
Copper (Cu), % 1.2 to 2.0
0
Iron (Fe), % 41.8 to 50.1
83.4 to 87.5
Manganese (Mn), % 1.0 to 2.5
0 to 1.0
Molybdenum (Mo), % 4.2 to 5.2
0
Nickel (Ni), % 24 to 26
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030