AWS E410NiMo vs. S21460 Stainless Steel

Both AWS E410NiMo and S21460 stainless steel are iron alloys. They have 78% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is AWS E410NiMo and the bottom bar is S21460 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 17
46
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
77
Tensile Strength: Ultimate (UTS), MPa 850
830

Thermal Properties

Latent Heat of Fusion, J/g 280
290
Melting Completion (Liquidus), °C 1440
1380
Melting Onset (Solidus), °C 1400
1330
Specific Heat Capacity, J/kg-K 480
480
Thermal Expansion, µm/m-K 14
18

Otherwise Unclassified Properties

Base Metal Price, % relative 10
14
Density, g/cm3 7.8
7.6
Embodied Carbon, kg CO2/kg material 2.4
3.0
Embodied Energy, MJ/kg 34
43
Embodied Water, L/kg 110
160

Common Calculations

PREN (Pitting Resistance) 14
25
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
30
Strength to Weight: Bending, points 26
26
Thermal Shock Resistance, points 23
17

Alloy Composition

Carbon (C), % 0 to 0.060
0 to 0.12
Chromium (Cr), % 11 to 12.5
17 to 19
Copper (Cu), % 0 to 0.75
0
Iron (Fe), % 79 to 84.6
57.3 to 63.7
Manganese (Mn), % 0 to 1.0
14 to 16
Molybdenum (Mo), % 0.4 to 0.7
0
Nickel (Ni), % 4.0 to 5.0
5.0 to 6.0
Nitrogen (N), % 0
0.35 to 0.5
Phosphorus (P), % 0 to 0.040
0 to 0.060
Silicon (Si), % 0 to 0.9
0 to 1.0
Sulfur (S), % 0 to 0.030
0 to 0.030