AWS E630 vs. R60901 Alloy
AWS E630 belongs to the iron alloys classification, while R60901 alloy belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.
For each property being compared, the top bar is AWS E630 and the bottom bar is R60901 alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 98 |
| Elongation at Break, % | 8.0 | |
| 17 to 22 |
| Poisson's Ratio | 0.28 | |
| 0.34 |
| Shear Modulus, GPa | 76 | |
| 37 |
| Tensile Strength: Ultimate (UTS), MPa | 1040 | |
| 500 to 580 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 270 |
| Thermal Conductivity, W/m-K | 17 | |
| 17 |
| Thermal Expansion, µm/m-K | 14 | |
| 6.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 6.6 |
| Embodied Water, L/kg | 140 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 8.3 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 37 | |
| 21 to 25 |
| Strength to Weight: Bending, points | 29 | |
| 21 to 24 |
| Thermal Diffusivity, mm2/s | 4.5 | |
| 9.7 |
| Thermal Shock Resistance, points | 28 | |
| 58 to 67 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 0 to 0.050 | |
| 0 |
| Chromium (Cr), % | 16 to 16.8 | |
| 0 |
| Copper (Cu), % | 3.3 to 4.0 | |
| 0 |
| Iron (Fe), % | 71.6 to 75.9 | |
| 0 |
| Manganese (Mn), % | 0.25 to 0.75 | |
| 0 |
| Molybdenum (Mo), % | 0 to 0.75 | |
| 0 |
| Nickel (Ni), % | 4.5 to 5.0 | |
| 0 |
| Niobium (Nb), % | 0.15 to 0.3 | |
| 2.4 to 2.8 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Zirconium (Zr), % | 0 | |
| 96.8 to 97.5 |
| Residuals, % | 0 | |
| 0 to 0.29 |