AWS E80C-Ni3 vs. EN 1.4508 Stainless Steel

Both AWS E80C-Ni3 and EN 1.4508 stainless steel are iron alloys. They have 70% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is AWS E80C-Ni3 and the bottom bar is EN 1.4508 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 27
34
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 72
79
Tensile Strength: Ultimate (UTS), MPa 630
570
Tensile Strength: Yield (Proof), MPa 530
260

Thermal Properties

Latent Heat of Fusion, J/g 260
300
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1410
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 51
15
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.4
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 3.9
20
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.7
4.0
Embodied Energy, MJ/kg 23
55
Embodied Water, L/kg 53
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 160
160
Resilience: Unit (Modulus of Resilience), kJ/m3 740
170
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
20
Strength to Weight: Bending, points 21
19
Thermal Diffusivity, mm2/s 14
4.1
Thermal Shock Resistance, points 19
17

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.12
0 to 0.030
Chromium (Cr), % 0
18 to 20
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 92.8 to 97.3
61.2 to 69.9
Manganese (Mn), % 0 to 1.5
0 to 1.5
Molybdenum (Mo), % 0
3.0 to 3.5
Nickel (Ni), % 2.8 to 3.8
9.0 to 12
Nitrogen (N), % 0
0.1 to 0.2
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.9
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.030
Vanadium (V), % 0 to 0.030
0
Residuals, % 0 to 0.5
0