AWS ENiCrCoMo-1 vs. AISI 434 Stainless Steel
AWS ENiCrCoMo-1 belongs to the nickel alloys classification, while AISI 434 stainless steel belongs to the iron alloys. They have a modest 21% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is AWS ENiCrCoMo-1 and the bottom bar is AISI 434 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 200 |
| Elongation at Break, % | 28 | |
| 24 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 82 | |
| 78 |
| Tensile Strength: Ultimate (UTS), MPa | 710 | |
| 520 |
Thermal Properties
| Latent Heat of Fusion, J/g | 330 | |
| 280 |
| Melting Completion (Liquidus), °C | 1430 | |
| 1510 |
| Melting Onset (Solidus), °C | 1380 | |
| 1430 |
| Specific Heat Capacity, J/kg-K | 440 | |
| 480 |
| Thermal Expansion, µm/m-K | 13 | |
| 10 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 75 | |
| 9.5 |
| Density, g/cm3 | 8.5 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 11 | |
| 2.4 |
| Embodied Energy, MJ/kg | 140 | |
| 33 |
| Embodied Water, L/kg | 340 | |
| 120 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 23 | |
| 25 |
| Strength to Weight: Axial, points | 23 | |
| 19 |
| Strength to Weight: Bending, points | 21 | |
| 18 |
| Thermal Shock Resistance, points | 19 | |
| 19 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Carbon (C), % | 0.050 to 0.15 | |
| 0 to 0.12 |
| Chromium (Cr), % | 21 to 26 | |
| 16 to 18 |
| Cobalt (Co), % | 9.0 to 15 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Iron (Fe), % | 0 to 5.0 | |
| 78.6 to 83.3 |
| Manganese (Mn), % | 0.3 to 2.5 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 8.0 to 10 | |
| 0.75 to 1.3 |
| Nickel (Ni), % | 38.6 to 61.7 | |
| 0 |
| Niobium (Nb), % | 0 to 1.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.75 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Residuals, % | 0 to 0.5 | |
| 0 |