AWS ER80S-B3L vs. AWS E312

Both AWS ER80S-B3L and AWS E312 are iron alloys. They have 62% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is AWS E312.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 19
25
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 74
80
Tensile Strength: Ultimate (UTS), MPa 630
740

Thermal Properties

Latent Heat of Fusion, J/g 260
310
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 13
15

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
20
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 1.8
3.6
Embodied Energy, MJ/kg 23
52
Embodied Water, L/kg 60
200

Common Calculations

PREN (Pitting Resistance) 6.0
31
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 22
27
Strength to Weight: Bending, points 21
24
Thermal Shock Resistance, points 18
18

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.050
0 to 0.15
Chromium (Cr), % 2.3 to 2.7
28 to 32
Copper (Cu), % 0 to 0.35
0 to 0.75
Iron (Fe), % 93.6 to 96
52.3 to 63.5
Manganese (Mn), % 0.4 to 0.7
0.5 to 2.5
Molybdenum (Mo), % 0.9 to 1.2
0 to 0.75
Nickel (Ni), % 0 to 0.2
8.0 to 10.5
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.4 to 0.7
0 to 1.0
Sulfur (S), % 0 to 0.025
0 to 0.030
Residuals, % 0 to 0.5
0