AWS ER80S-B3L vs. SAE-AISI 1090 Steel

Both AWS ER80S-B3L and SAE-AISI 1090 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is AWS ER80S-B3L and the bottom bar is SAE-AISI 1090 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 19
11
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 630
790 to 950
Tensile Strength: Yield (Proof), MPa 530
520 to 610

Thermal Properties

Latent Heat of Fusion, J/g 260
240
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 41
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.7
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.9
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 4.1
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 23
19
Embodied Water, L/kg 60
46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
82 to 91
Resilience: Unit (Modulus of Resilience), kJ/m3 730
730 to 1000
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 22
28 to 34
Strength to Weight: Bending, points 21
24 to 27
Thermal Diffusivity, mm2/s 11
13
Thermal Shock Resistance, points 18
25 to 31

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.050
0.85 to 1.0
Chromium (Cr), % 2.3 to 2.7
0
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 93.6 to 96
98 to 98.6
Manganese (Mn), % 0.4 to 0.7
0.6 to 0.9
Molybdenum (Mo), % 0.9 to 1.2
0
Nickel (Ni), % 0 to 0.2
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0.4 to 0.7
0
Sulfur (S), % 0 to 0.025
0 to 0.050
Residuals, % 0 to 0.5
0