AWS ERNiCrCoMo-1 vs. AWS ER120S-1

AWS ERNiCrCoMo-1 belongs to the nickel alloys classification, while AWS ER120S-1 belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrCoMo-1 and the bottom bar is AWS ER120S-1.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 28
17
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 710
930

Thermal Properties

Latent Heat of Fusion, J/g 330
260
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 450
470
Thermal Conductivity, W/m-K 13
46
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.8
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 75
4.2
Density, g/cm3 8.5
7.8
Embodied Carbon, kg CO2/kg material 10
1.9
Embodied Energy, MJ/kg 140
25
Embodied Water, L/kg 350
56

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 23
24
Strength to Weight: Axial, points 23
33
Strength to Weight: Bending, points 21
27
Thermal Diffusivity, mm2/s 3.5
13
Thermal Shock Resistance, points 19
27

Alloy Composition

Aluminum (Al), % 0.8 to 1.5
0 to 0.1
Carbon (C), % 0.050 to 0.15
0 to 0.1
Chromium (Cr), % 20 to 24
0 to 0.6
Cobalt (Co), % 10 to 15
0
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 3.0
92.4 to 96.1
Manganese (Mn), % 0 to 1.0
1.4 to 1.8
Molybdenum (Mo), % 8.0 to 10
0.3 to 0.65
Nickel (Ni), % 42.7 to 61.2
2.0 to 2.8
Phosphorus (P), % 0 to 0.030
0 to 0.010
Silicon (Si), % 0 to 1.0
0.25 to 0.6
Sulfur (S), % 0 to 0.015
0 to 0.010
Titanium (Ti), % 0 to 0.6
0 to 0.1
Vanadium (V), % 0
0 to 0.030
Zirconium (Zr), % 0
0 to 0.1
Residuals, % 0 to 0.5
0 to 0.5