AWS ERNiCrFe-6 vs. EN 1.4003 Stainless Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while EN 1.4003 stainless steel belongs to the iron alloys. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is EN 1.4003 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 34
22
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 74
76
Tensile Strength: Ultimate (UTS), MPa 630
540

Thermal Properties

Latent Heat of Fusion, J/g 310
270
Melting Completion (Liquidus), °C 1370
1440
Melting Onset (Solidus), °C 1320
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 13
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 55
6.5
Density, g/cm3 8.4
7.8
Embodied Carbon, kg CO2/kg material 9.8
1.9
Embodied Energy, MJ/kg 140
27
Embodied Water, L/kg 260
97

Common Calculations

Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 21
19
Strength to Weight: Bending, points 19
19
Thermal Diffusivity, mm2/s 3.3
6.7
Thermal Shock Resistance, points 19
19

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.080
0 to 0.030
Chromium (Cr), % 14 to 17
10.5 to 12.5
Copper (Cu), % 0 to 0.5
0
Iron (Fe), % 0 to 8.0
83.9 to 89.2
Manganese (Mn), % 2.0 to 2.7
0 to 1.5
Nickel (Ni), % 67 to 81.5
0.3 to 1.0
Nitrogen (N), % 0
0 to 0.030
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.35
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 2.5 to 3.5
0
Residuals, % 0 to 0.5
0