AWS ERNiCrFe-6 vs. EN 2.4668 Nickel

Both AWS ERNiCrFe-6 and EN 2.4668 nickel are nickel alloys. They have 73% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is EN 2.4668 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 34
14
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
75
Tensile Strength: Ultimate (UTS), MPa 630
1390

Thermal Properties

Latent Heat of Fusion, J/g 310
310
Melting Completion (Liquidus), °C 1370
1460
Melting Onset (Solidus), °C 1320
1410
Specific Heat Capacity, J/kg-K 460
450
Thermal Conductivity, W/m-K 13
13
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
1.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
1.5

Otherwise Unclassified Properties

Base Metal Price, % relative 55
75
Density, g/cm3 8.4
8.3
Embodied Carbon, kg CO2/kg material 9.8
13
Embodied Energy, MJ/kg 140
190
Embodied Water, L/kg 260
250

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
23
Strength to Weight: Axial, points 21
46
Strength to Weight: Bending, points 19
33
Thermal Diffusivity, mm2/s 3.3
3.5
Thermal Shock Resistance, points 19
40

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Aluminum (Al), % 0
0.3 to 0.7
Boron (B), % 0
0.0020 to 0.0060
Carbon (C), % 0 to 0.080
0.020 to 0.080
Chromium (Cr), % 14 to 17
17 to 21
Cobalt (Co), % 0
0 to 1.0
Copper (Cu), % 0 to 0.5
0 to 0.3
Iron (Fe), % 0 to 8.0
11.2 to 24.6
Manganese (Mn), % 2.0 to 2.7
0 to 0.35
Molybdenum (Mo), % 0
2.8 to 3.3
Nickel (Ni), % 67 to 81.5
50 to 55
Niobium (Nb), % 0
4.7 to 5.5
Phosphorus (P), % 0 to 0.030
0 to 0.015
Silicon (Si), % 0 to 0.35
0 to 0.35
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 2.5 to 3.5
0.6 to 1.2
Residuals, % 0 to 0.5
0