AWS ERNiCrFe-6 vs. SAE-AISI S5 Steel

AWS ERNiCrFe-6 belongs to the nickel alloys classification, while SAE-AISI S5 steel belongs to the iron alloys. There are 23 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is AWS ERNiCrFe-6 and the bottom bar is SAE-AISI S5 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 74
72
Tensile Strength: Ultimate (UTS), MPa 630
680 to 1940

Thermal Properties

Latent Heat of Fusion, J/g 310
280
Melting Completion (Liquidus), °C 1370
1440
Melting Onset (Solidus), °C 1320
1400
Specific Heat Capacity, J/kg-K 460
480
Thermal Conductivity, W/m-K 13
42
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.4
7.4
Electrical Conductivity: Equal Weight (Specific), % IACS 1.5
8.7

Otherwise Unclassified Properties

Base Metal Price, % relative 55
3.1
Density, g/cm3 8.4
7.7
Embodied Carbon, kg CO2/kg material 9.8
2.1
Embodied Energy, MJ/kg 140
29
Embodied Water, L/kg 260
51

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 23
25
Strength to Weight: Axial, points 21
25 to 70
Strength to Weight: Bending, points 19
22 to 45
Thermal Diffusivity, mm2/s 3.3
11
Thermal Shock Resistance, points 19
23 to 65

Alloy Composition


Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
Carbon (C), % 0 to 0.080
0.5 to 0.65
Chromium (Cr), % 14 to 17
0 to 0.5
Copper (Cu), % 0 to 0.5
0 to 0.25
Iron (Fe), % 0 to 8.0
93.6 to 97
Manganese (Mn), % 2.0 to 2.7
0.6 to 1.0
Molybdenum (Mo), % 0
0.2 to 1.4
Nickel (Ni), % 67 to 81.5
0
Phosphorus (P), % 0 to 0.030
0 to 0.030
Silicon (Si), % 0 to 0.35
1.8 to 2.3
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 2.5 to 3.5
0
Vanadium (V), % 0
0 to 0.35
Residuals, % 0 to 0.5
0