AWS ERNiMo-3 vs. Grade 24 Titanium
AWS ERNiMo-3 belongs to the nickel alloys classification, while grade 24 titanium belongs to the titanium alloys. There are 18 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.
For each property being compared, the top bar is AWS ERNiMo-3 and the bottom bar is grade 24 titanium.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 110 |
| Poisson's Ratio | 0.3 | |
| 0.32 |
| Shear Modulus, GPa | 83 | |
| 40 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 1010 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 410 |
| Melting Completion (Liquidus), °C | 1600 | |
| 1610 |
| Melting Onset (Solidus), °C | 1540 | |
| 1560 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 560 |
| Thermal Expansion, µm/m-K | 11 | |
| 9.6 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 4.5 |
| Embodied Carbon, kg CO2/kg material | 15 | |
| 43 |
| Embodied Energy, MJ/kg | 190 | |
| 710 |
| Embodied Water, L/kg | 270 | |
| 310 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 22 | |
| 35 |
| Strength to Weight: Axial, points | 24 | |
| 63 |
| Strength to Weight: Bending, points | 21 | |
| 50 |
| Thermal Shock Resistance, points | 24 | |
| 72 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 5.5 to 6.8 |
| Carbon (C), % | 0 to 0.12 | |
| 0 to 0.080 |
| Chromium (Cr), % | 4.0 to 6.0 | |
| 0 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 |
| Hydrogen (H), % | 0 | |
| 0 to 0.015 |
| Iron (Fe), % | 4.0 to 7.0 | |
| 0 to 0.4 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 23 to 26 | |
| 0 |
| Nickel (Ni), % | 53.7 to 69 | |
| 0 |
| Nitrogen (N), % | 0 | |
| 0 to 0.050 |
| Oxygen (O), % | 0 | |
| 0 to 0.2 |
| Palladium (Pd), % | 0 | |
| 0.040 to 0.080 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Titanium (Ti), % | 0 | |
| 87.5 to 91 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |
| Vanadium (V), % | 0 to 0.6 | |
| 3.5 to 4.5 |
| Residuals, % | 0 to 0.5 | |
| 0 to 0.4 |