AWS ERNiMo-3 vs. Solder Alloy 181
AWS ERNiMo-3 belongs to the nickel alloys classification, while solder alloy 181 belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.
For each property being compared, the top bar is AWS ERNiMo-3 and the bottom bar is solder alloy 181.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 220 | |
| 18 |
| Poisson's Ratio | 0.3 | |
| 0.44 |
| Shear Modulus, GPa | 83 | |
| 6.1 |
| Tensile Strength: Ultimate (UTS), MPa | 770 | |
| 27 |
Thermal Properties
| Latent Heat of Fusion, J/g | 320 | |
| 26 |
| Melting Completion (Liquidus), °C | 1600 | |
| 310 |
| Melting Onset (Solidus), °C | 1540 | |
| 300 |
| Specific Heat Capacity, J/kg-K | 400 | |
| 130 |
| Thermal Expansion, µm/m-K | 11 | |
| 29 |
Otherwise Unclassified Properties
| Density, g/cm3 | 9.1 | |
| 11 |
| Embodied Carbon, kg CO2/kg material | 15 | |
| 6.2 |
| Embodied Energy, MJ/kg | 190 | |
| 100 |
Common Calculations
| Stiffness to Weight: Axial, points | 13 | |
| 0.86 |
| Stiffness to Weight: Bending, points | 22 | |
| 7.7 |
| Strength to Weight: Axial, points | 24 | |
| 0.66 |
| Strength to Weight: Bending, points | 21 | |
| 1.8 |
| Thermal Shock Resistance, points | 24 | |
| 3.8 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 452
| Aluminum (Al), % | 0 | |
| 0 to 0.0010 |
| Antimony (Sb), % | 0 | |
| 0 to 0.2 |
| Arsenic (As), % | 0 | |
| 0 to 0.030 |
| Bismuth (Bi), % | 0 | |
| 0 to 0.1 |
| Cadmium (Cd), % | 0 | |
| 0 to 0.0020 |
| Carbon (C), % | 0 to 0.12 | |
| 0 |
| Chromium (Cr), % | 4.0 to 6.0 | |
| 0 |
| Cobalt (Co), % | 0 to 2.5 | |
| 0 |
| Copper (Cu), % | 0 to 0.5 | |
| 0 to 0.080 |
| Gold (Au), % | 0 | |
| 0 to 0.050 |
| Indium (In), % | 0 | |
| 0 to 0.1 |
| Iron (Fe), % | 4.0 to 7.0 | |
| 0 to 0.020 |
| Lead (Pb), % | 0 | |
| 96.2 to 98 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0 |
| Molybdenum (Mo), % | 23 to 26 | |
| 0 |
| Nickel (Ni), % | 53.7 to 69 | |
| 0 to 0.010 |
| Phosphorus (P), % | 0 to 0.040 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 |
| Silver (Ag), % | 0 | |
| 2.0 to 3.0 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 |
| Tin (Sn), % | 0 | |
| 0 to 0.25 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |
| Vanadium (V), % | 0 to 0.6 | |
| 0 |
| Zinc (Zn), % | 0 | |
| 0 to 0.0010 |
| Residuals, % | 0 to 0.5 | |
| 0 |