AZ91B Magnesium vs. SAE-AISI 5140 Steel

AZ91B magnesium belongs to the magnesium alloys classification, while SAE-AISI 5140 steel belongs to the iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is AZ91B magnesium and the bottom bar is SAE-AISI 5140 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 63
170 to 290
Elastic (Young's, Tensile) Modulus, GPa 46
190
Elongation at Break, % 5.0
12 to 29
Fatigue Strength, MPa 79
220 to 570
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 18
73
Shear Strength, MPa 140
360 to 600
Tensile Strength: Ultimate (UTS), MPa 240
560 to 970
Tensile Strength: Yield (Proof), MPa 160
290 to 840

Thermal Properties

Latent Heat of Fusion, J/g 360
250
Maximum Temperature: Mechanical, °C 130
420
Melting Completion (Liquidus), °C 600
1460
Melting Onset (Solidus), °C 470
1420
Specific Heat Capacity, J/kg-K 990
470
Thermal Conductivity, W/m-K 73
45
Thermal Expansion, µm/m-K 26
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 11
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 58
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
2.1
Density, g/cm3 1.7
7.8
Embodied Carbon, kg CO2/kg material 22
1.4
Embodied Energy, MJ/kg 160
19
Embodied Water, L/kg 990
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 11
76 to 180
Resilience: Unit (Modulus of Resilience), kJ/m3 280
220 to 1880
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 69
24
Strength to Weight: Axial, points 38
20 to 34
Strength to Weight: Bending, points 49
19 to 28
Thermal Diffusivity, mm2/s 42
12
Thermal Shock Resistance, points 14
16 to 29

Alloy Composition

Aluminum (Al), % 8.3 to 9.7
0
Carbon (C), % 0
0.38 to 0.43
Chromium (Cr), % 0
0.7 to 0.9
Copper (Cu), % 0 to 0.35
0
Iron (Fe), % 0
97.3 to 98.1
Magnesium (Mg), % 87.9 to 91.2
0
Manganese (Mn), % 0.13 to 0.5
0.7 to 0.9
Nickel (Ni), % 0 to 0.030
0
Phosphorus (P), % 0
0 to 0.035
Silicon (Si), % 0 to 0.5
0.15 to 0.35
Sulfur (S), % 0
0 to 0.040
Zinc (Zn), % 0.35 to 1.0
0