Annealed SAE-AISI 4320 vs. Annealed AISI 440A
Both annealed SAE-AISI 4320 and annealed AISI 440A are iron alloys. Both are furnished in the annealed condition. They have 83% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.
For each property being compared, the top bar is annealed SAE-AISI 4320 and the bottom bar is annealed AISI 440A.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 200 |
| Elongation at Break, % | 29 | |
| 20 |
| Fatigue Strength, MPa | 320 | |
| 270 |
| Poisson's Ratio | 0.29 | |
| 0.28 |
| Shear Modulus, GPa | 73 | |
| 77 |
| Shear Strength, MPa | 370 | |
| 450 |
| Tensile Strength: Ultimate (UTS), MPa | 570 | |
| 730 |
| Tensile Strength: Yield (Proof), MPa | 430 | |
| 420 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 280 |
| Maximum Temperature: Mechanical, °C | 420 | |
| 760 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1480 |
| Melting Onset (Solidus), °C | 1420 | |
| 1370 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 480 |
| Thermal Conductivity, W/m-K | 46 | |
| 23 |
| Thermal Expansion, µm/m-K | 11 | |
| 10 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 2.5 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 2.9 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 3.4 | |
| 9.0 |
| Density, g/cm3 | 7.9 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 1.7 | |
| 2.2 |
| Embodied Energy, MJ/kg | 22 | |
| 31 |
| Embodied Water, L/kg | 52 | |
| 120 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 | |
| 120 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 480 | |
| 440 |
| Stiffness to Weight: Axial, points | 13 | |
| 14 |
| Stiffness to Weight: Bending, points | 24 | |
| 25 |
| Strength to Weight: Axial, points | 20 | |
| 26 |
| Strength to Weight: Bending, points | 19 | |
| 23 |
| Thermal Diffusivity, mm2/s | 13 | |
| 6.2 |
| Thermal Shock Resistance, points | 19 | |
| 26 |
Alloy Composition
| Carbon (C), % | 0.17 to 0.22 | |
| 0.6 to 0.75 |
| Chromium (Cr), % | 0.4 to 0.6 | |
| 16 to 18 |
| Iron (Fe), % | 95.8 to 97 | |
| 78.4 to 83.4 |
| Manganese (Mn), % | 0.45 to 0.65 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 0.2 to 0.3 | |
| 0 to 0.75 |
| Nickel (Ni), % | 1.7 to 2.0 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.040 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0 to 1.0 |
| Sulfur (S), % | 0 to 0.040 | |
| 0 to 0.015 |