Annealed SAE-AISI 52100 vs. Annealed SAE-AISI L3
Both annealed SAE-AISI 52100 and annealed SAE-AISI L3 are iron alloys. Both are furnished in the annealed condition. Their average alloy composition is basically identical. There are 30 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.
For each property being compared, the top bar is annealed SAE-AISI 52100 and the bottom bar is annealed SAE-AISI L3.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 180 | |
| 180 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Elongation at Break, % | 20 | |
| 21 |
| Fatigue Strength, MPa | 250 | |
| 230 |
| Poisson's Ratio | 0.29 | |
| 0.29 |
| Shear Modulus, GPa | 72 | |
| 72 |
| Shear Strength, MPa | 370 | |
| 380 |
| Tensile Strength: Ultimate (UTS), MPa | 590 | |
| 600 |
| Tensile Strength: Yield (Proof), MPa | 360 | |
| 330 |
Thermal Properties
| Latent Heat of Fusion, J/g | 250 | |
| 250 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1450 |
| Melting Onset (Solidus), °C | 1410 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 47 | |
| 43 |
| Thermal Expansion, µm/m-K | 12 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.3 | |
| 7.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.5 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 2.4 | |
| 2.5 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 1.5 | |
| 1.9 |
| Embodied Energy, MJ/kg | 20 | |
| 27 |
| Embodied Water, L/kg | 51 | |
| 53 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 100 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 350 | |
| 300 |
| Stiffness to Weight: Axial, points | 13 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 21 | |
| 21 |
| Strength to Weight: Bending, points | 20 | |
| 20 |
| Thermal Diffusivity, mm2/s | 13 | |
| 12 |
| Thermal Shock Resistance, points | 19 | |
| 18 |
Alloy Composition
| Carbon (C), % | 0.93 to 1.1 | |
| 1.0 to 1.1 |
| Chromium (Cr), % | 1.4 to 1.6 | |
| 1.3 to 1.7 |
| Iron (Fe), % | 96.5 to 97.3 | |
| 95.5 to 97.3 |
| Manganese (Mn), % | 0.25 to 0.45 | |
| 0.25 to 0.8 |
| Phosphorus (P), % | 0 to 0.025 | |
| 0 to 0.030 |
| Silicon (Si), % | 0.15 to 0.35 | |
| 0.1 to 0.5 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.030 |
| Vanadium (V), % | 0 | |
| 0.1 to 0.3 |