Annealed 86.5-silver 13.5-cadmium-oxide vs. Annealed ASTM B522 Class I
Both annealed 86.5-silver 13.5-cadmium-oxide and annealed ASTM B522 class I are otherwise unclassified metals. Both are furnished in the annealed condition. There are 8 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.
For each property being compared, the top bar is annealed 86.5-silver 13.5-cadmium-oxide and the bottom bar is annealed ASTM B522 class I.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 17 |
| Electrical Conductivity: Equal Volume, % IACS | 85 | |
| 11 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 76 | |
| 5.8 |
| Elongation at Break, % | 16 | |
| 29 |
| Shear Strength, MPa | 170 | |
| 180 |
| Strength to Weight: Axial, points | 7.6 | |
| 4.4 |
| Strength to Weight: Bending, points | 9.3 | |
| 5.5 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 280 |