Annealed 86.5-silver 13.5-cadmium-oxide vs. Annealed Nickel 201
Annealed 86.5-silver 13.5-cadmium-oxide belongs to the otherwise unclassified metals classification, while annealed nickel 201 belongs to the nickel alloys. There are 8 material properties with values for both materials. Properties with values for just one material (24, in this case) are not shown.
For each property being compared, the top bar is annealed 86.5-silver 13.5-cadmium-oxide and the bottom bar is annealed nickel 201.
Metric UnitsUS Customary Units
Material Properties
| Density, g/cm3 | 10 | |
| 8.9 |
| Electrical Conductivity: Equal Volume, % IACS | 85 | |
| 19 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 76 | |
| 19 |
| Elongation at Break, % | 16 | |
| 43 |
| Shear Strength, MPa | 170 | |
| 270 |
| Strength to Weight: Axial, points | 7.6 | |
| 12 |
| Strength to Weight: Bending, points | 9.3 | |
| 13 |
| Tensile Strength: Ultimate (UTS), MPa | 280 | |
| 400 |