Annealed K93600 vs. Annealed S35000 Stainless Steel

Both annealed K93600 and annealed S35000 stainless steel are iron alloys. Both are furnished in the annealed condition. There are 21 material properties with values for both materials. Properties with values for just one material (15, in this case) are not shown.

For each property being compared, the top bar is annealed K93600 and the bottom bar is annealed S35000 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 140
200
Elongation at Break, % 35
14
Shear Strength, MPa 320
950
Tensile Strength: Ultimate (UTS), MPa 480
1570
Tensile Strength: Yield (Proof), MPa 280
660

Thermal Properties

Maximum Temperature: Mechanical, °C 440
900
Melting Onset (Solidus), °C 1430
1410
Specific Heat Capacity, J/kg-K 520
470
Thermal Conductivity, W/m-K 13
16
Thermal Expansion, µm/m-K 7.3
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
2.6

Otherwise Unclassified Properties

Density, g/cm3 8.1
7.8

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
170
Resilience: Unit (Modulus of Resilience), kJ/m3 280
1070
Stiffness to Weight: Axial, points 9.4
14
Stiffness to Weight: Bending, points 21
25
Strength to Weight: Axial, points 16
56
Strength to Weight: Bending, points 17
38
Thermal Diffusivity, mm2/s 3.1
4.4
Thermal Shock Resistance, points 34
51