Annealed Monel R-405 vs. Annealed R30605 Cobalt
Annealed Monel R-405 belongs to the nickel alloys classification, while annealed R30605 cobalt belongs to the cobalt alloys. There are 27 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is annealed Monel R-405 and the bottom bar is annealed R30605 cobalt.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 160 | |
| 210 |
| Elongation at Break, % | 39 | |
| 34 |
| Fatigue Strength, MPa | 210 | |
| 260 |
| Poisson's Ratio | 0.32 | |
| 0.29 |
| Shear Modulus, GPa | 62 | |
| 81 |
| Tensile Strength: Ultimate (UTS), MPa | 540 | |
| 1130 |
| Tensile Strength: Yield (Proof), MPa | 190 | |
| 470 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 290 |
| Melting Completion (Liquidus), °C | 1350 | |
| 1410 |
| Melting Onset (Solidus), °C | 1300 | |
| 1330 |
| Specific Heat Capacity, J/kg-K | 430 | |
| 410 |
| Thermal Conductivity, W/m-K | 23 | |
| 9.6 |
| Thermal Expansion, µm/m-K | 14 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 3.4 | |
| 2.0 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 3.4 | |
| 1.8 |
Otherwise Unclassified Properties
| Density, g/cm3 | 8.9 | |
| 9.6 |
| Embodied Carbon, kg CO2/kg material | 7.9 | |
| 9.8 |
| Embodied Energy, MJ/kg | 110 | |
| 140 |
| Embodied Water, L/kg | 250 | |
| 450 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 170 | |
| 310 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 120 | |
| 520 |
| Stiffness to Weight: Axial, points | 10 | |
| 12 |
| Stiffness to Weight: Bending, points | 21 | |
| 21 |
| Strength to Weight: Axial, points | 17 | |
| 33 |
| Strength to Weight: Bending, points | 17 | |
| 25 |
| Thermal Diffusivity, mm2/s | 5.9 | |
| 2.5 |
| Thermal Shock Resistance, points | 17 | |
| 31 |
Alloy Composition
| Carbon (C), % | 0 to 0.3 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 0 | |
| 19 to 21 |
| Cobalt (Co), % | 0 | |
| 46.4 to 57 |
| Copper (Cu), % | 28 to 34 | |
| 0 |
| Iron (Fe), % | 0 to 2.5 | |
| 0 to 3.0 |
| Manganese (Mn), % | 0 to 2.0 | |
| 1.0 to 2.0 |
| Nickel (Ni), % | 63 to 72 | |
| 9.0 to 11 |
| Phosphorus (P), % | 0 | |
| 0 to 0.040 |
| Silicon (Si), % | 0 to 0.5 | |
| 0 to 0.4 |
| Sulfur (S), % | 0.025 to 0.060 | |
| 0 to 0.030 |
| Tungsten (W), % | 0 | |
| 14 to 16 |