Austempered Cast Iron vs. EN 1.7034 Steel

Both austempered cast iron and EN 1.7034 steel are iron alloys. They have a moderately high 93% of their average alloy composition in common. There are 22 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is austempered cast iron and the bottom bar is EN 1.7034 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 270 to 490
150 to 250
Elastic (Young's, Tensile) Modulus, GPa 180
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 62 to 69
73
Tensile Strength: Ultimate (UTS), MPa 860 to 1800
510 to 1780

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Melting Completion (Liquidus), °C 1380
1460
Melting Onset (Solidus), °C 1340
1420
Specific Heat Capacity, J/kg-K 490
470
Thermal Conductivity, W/m-K 42
45
Thermal Expansion, µm/m-K 13
13

Otherwise Unclassified Properties

Base Metal Price, % relative 2.9
2.2
Density, g/cm3 7.5
7.8
Embodied Carbon, kg CO2/kg material 1.8
1.4
Embodied Energy, MJ/kg 25
19
Embodied Water, L/kg 48
50

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 32 to 66
18 to 63
Strength to Weight: Bending, points 27 to 44
18 to 42
Thermal Diffusivity, mm2/s 11
12
Thermal Shock Resistance, points 25 to 53
15 to 52

Alloy Composition

Aluminum (Al), % 0 to 0.050
0
Arsenic (As), % 0 to 0.020
0
Carbon (C), % 3.4 to 3.8
0.34 to 0.41
Chromium (Cr), % 0 to 0.1
0.9 to 1.2
Copper (Cu), % 0 to 0.8
0
Iron (Fe), % 89.6 to 94
97 to 98.2
Magnesium (Mg), % 0 to 0.040
0
Manganese (Mn), % 0.3 to 0.4
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.3
0
Nickel (Ni), % 0 to 2.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.035
Selenium (Se), % 0 to 0.030
0
Silicon (Si), % 2.3 to 2.7
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.035
Tin (Sn), % 0 to 0.020
0
Vanadium (V), % 0 to 0.1
0