Cold Worked R05200 Tantalum vs. Work Hardened 92-silver 8-tin-oxide
Both cold worked R05200 tantalum and work hardened 92-silver 8-tin-oxide are otherwise unclassified metals. Both are furnished in the cold worked (strain hardened) condition. There are 4 material properties with values for both materials. Properties with values for just one material (19, in this case) are not shown.
For each property being compared, the top bar is cold worked R05200 tantalum and the bottom bar is work hardened 92-silver 8-tin-oxide.
Metric UnitsUS Customary Units
Material Properties
Elongation at Break, % | 1.1 | |
34 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 5.5 | |
110 |
Tensile Strength: Ultimate (UTS), MPa | 540 | |
320 |
Tensile Strength: Yield (Proof), MPa | 390 | |
300 |