Ductile Cast Iron vs. 70Ag-30Ni Alloy
Ductile cast iron belongs to the iron alloys classification, while 70Ag-30Ni alloy belongs to the otherwise unclassified metals. There are 17 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is ductile cast iron and the bottom bar is 70Ag-30Ni alloy.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 170 to 180 | |
| 100 |
| Poisson's Ratio | 0.28 to 0.31 | |
| 0.35 |
| Shear Modulus, GPa | 64 to 70 | |
| 39 |
| Tensile Strength: Ultimate (UTS), MPa | 460 to 920 | |
| 320 to 530 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 170 |
| Melting Completion (Liquidus), °C | 1160 | |
| 960 |
| Melting Onset (Solidus), °C | 1120 | |
| 960 |
| Specific Heat Capacity, J/kg-K | 490 | |
| 300 |
| Thermal Expansion, µm/m-K | 11 | |
| 17 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 7.4 | |
| 69 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 8.8 to 9.4 | |
| 62 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.1 to 7.5 | |
| 10 |
Common Calculations
| Stiffness to Weight: Axial, points | 12 to 14 | |
| 5.8 |
| Stiffness to Weight: Bending, points | 24 to 26 | |
| 16 |
| Strength to Weight: Axial, points | 17 to 35 | |
| 8.8 to 15 |
| Strength to Weight: Bending, points | 18 to 29 | |
| 10 to 15 |
| Thermal Shock Resistance, points | 17 to 35 | |
| 13 to 21 |
Alloy Composition
Deprecated: Automatic conversion of false to array is deprecated in /home/public/compare.php on line 460
| Carbon (C), % | 3.0 to 3.5 | |
| 0 |
| Iron (Fe), % | 93.7 to 95.5 | |
| 0 |
| Nickel (Ni), % | 0 | |
| 28.8 to 31 |
| Phosphorus (P), % | 0 to 0.080 | |
| 0 |
| Silicon (Si), % | 1.5 to 2.8 | |
| 0 |
| Silver (Ag), % | 0 | |
| 69 to 71 |
| Residuals, % | 0 | |
| 0 to 0.2 |