EN 1.0031 Steel vs. SAE-AISI H23 Steel

Both EN 1.0031 steel and SAE-AISI H23 steel are iron alloys. They have 75% of their average alloy composition in common. There are 21 material properties with values for both materials. Properties with values for just one material (11, in this case) are not shown.

For each property being compared, the top bar is EN 1.0031 steel and the bottom bar is SAE-AISI H23 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
80
Tensile Strength: Ultimate (UTS), MPa 310
760 to 1550

Thermal Properties

Latent Heat of Fusion, J/g 250
260
Melting Completion (Liquidus), °C 1470
1680
Melting Onset (Solidus), °C 1420
1630
Specific Heat Capacity, J/kg-K 470
440
Thermal Conductivity, W/m-K 53
20
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
34
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 1.4
6.9
Embodied Energy, MJ/kg 18
110
Embodied Water, L/kg 45
120

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
22
Strength to Weight: Axial, points 11
24 to 49
Strength to Weight: Bending, points 13
21 to 34
Thermal Diffusivity, mm2/s 14
5.2
Thermal Shock Resistance, points 9.8
23 to 47

Alloy Composition

Carbon (C), % 0 to 0.1
0.25 to 0.35
Chromium (Cr), % 0
11 to 12.8
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 98.8 to 100
71.3 to 76.7
Manganese (Mn), % 0 to 0.7
0.15 to 0.4
Nickel (Ni), % 0
0 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.030
Silicon (Si), % 0 to 0.35
0.15 to 0.6
Sulfur (S), % 0 to 0.045
0 to 0.030
Tungsten (W), % 0
11 to 12.8
Vanadium (V), % 0
0.75 to 1.3