EN 1.0034 Steel vs. AISI 310 Stainless Steel

Both EN 1.0034 steel and AISI 310 stainless steel are iron alloys. They have 53% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0034 steel and the bottom bar is AISI 310 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 97 to 110
180 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 9.0 to 32
34 to 45
Fatigue Strength, MPa 140 to 170
240 to 280
Poisson's Ratio 0.29
0.27
Shear Modulus, GPa 73
78
Shear Strength, MPa 220 to 230
420 to 470
Tensile Strength: Ultimate (UTS), MPa 340 to 380
600 to 710
Tensile Strength: Yield (Proof), MPa 180 to 280
260 to 350

Thermal Properties

Latent Heat of Fusion, J/g 250
310
Maximum Temperature: Mechanical, °C 400
1040
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 53
15
Thermal Expansion, µm/m-K 12
15

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
2.5

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
25
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
4.3
Embodied Energy, MJ/kg 18
61
Embodied Water, L/kg 45
190

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31 to 95
200 to 220
Resilience: Unit (Modulus of Resilience), kJ/m3 84 to 210
170 to 310
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 12 to 13
21 to 25
Strength to Weight: Bending, points 14 to 15
20 to 22
Thermal Diffusivity, mm2/s 14
3.9
Thermal Shock Resistance, points 11 to 12
14 to 17

Alloy Composition

Carbon (C), % 0 to 0.15
0 to 0.25
Chromium (Cr), % 0
24 to 26
Iron (Fe), % 98.7 to 100
48.2 to 57
Manganese (Mn), % 0 to 0.7
0 to 2.0
Nickel (Ni), % 0
19 to 22
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 0.35
0 to 1.5
Sulfur (S), % 0 to 0.045
0 to 0.030

Comparable Variants