EN 1.0034 Steel vs. SAE-AISI 8630 Steel

Both EN 1.0034 steel and SAE-AISI 8630 steel are iron alloys. They have a very high 98% of their average alloy composition in common.

For each property being compared, the top bar is EN 1.0034 steel and the bottom bar is SAE-AISI 8630 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 97 to 110
160 to 200
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 9.0 to 32
12 to 24
Fatigue Strength, MPa 140 to 170
260 to 350
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 220 to 230
340 to 410
Tensile Strength: Ultimate (UTS), MPa 340 to 380
540 to 680
Tensile Strength: Yield (Proof), MPa 180 to 280
360 to 560

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
39
Thermal Expansion, µm/m-K 12
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.0
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.0
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
2.6
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 18
20
Embodied Water, L/kg 45
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31 to 95
78 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 84 to 210
340 to 840
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 12 to 13
19 to 24
Strength to Weight: Bending, points 14 to 15
19 to 22
Thermal Diffusivity, mm2/s 14
10
Thermal Shock Resistance, points 11 to 12
18 to 23

Alloy Composition

Carbon (C), % 0 to 0.15
0.28 to 0.33
Chromium (Cr), % 0
0.4 to 0.6
Iron (Fe), % 98.7 to 100
96.8 to 97.9
Manganese (Mn), % 0 to 0.7
0.7 to 0.9
Molybdenum (Mo), % 0
0.15 to 0.25
Nickel (Ni), % 0
0.4 to 0.7
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.35
0.15 to 0.35
Sulfur (S), % 0 to 0.045
0 to 0.040

Comparable Variants