EN 1.0034 steel belongs to the iron alloys classification, while N07041 nickel belongs to the nickel alloys. There are 19 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0034 steel and the bottom bar is N07041 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
220
Elongation at Break, % 9.0 to 32
14
Fatigue Strength, MPa 140 to 170
540
Shear Strength, MPa 220 to 230
850
Tensile Strength: Ultimate (UTS), MPa 340 to 380
1400
Tensile Strength: Yield (Proof), MPa 180 to 280
1050

Thermal Properties

Melting Onset (Solidus), °C 1420
1320
Specific Heat Capacity, J/kg-K 470
450
Thermal Conductivity, W/m-K 53
11
Thermal Expansion, µm/m-K 12
12

Otherwise Unclassified Properties

Density, g/cm3 7.9
8.2

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 31 to 95
180
Resilience: Unit (Modulus of Resilience), kJ/m3 84 to 210
2510
Stiffness to Weight: Axial, points 13
15
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 12 to 13
47
Strength to Weight: Bending, points 14 to 15
34
Thermal Diffusivity, mm2/s 14
3.0
Thermal Shock Resistance, points 11 to 12
38