EN 1.0038 Steel vs. SAE-AISI 1541 Steel

Both EN 1.0038 steel and SAE-AISI 1541 steel are iron alloys. They have a very high 99% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0038 steel and the bottom bar is SAE-AISI 1541 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 120
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23 to 25
11 to 17
Fatigue Strength, MPa 140 to 160
260 to 420
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 240 to 270
440 to 480
Tensile Strength: Ultimate (UTS), MPa 380 to 430
720 to 790
Tensile Strength: Yield (Proof), MPa 200 to 220
390 to 680

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 48
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72 to 88
78 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 110 to 130
410 to 1250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13 to 15
25 to 28
Strength to Weight: Bending, points 15 to 16
23 to 24
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 12 to 13
23 to 25

Alloy Composition

Carbon (C), % 0 to 0.23
0.36 to 0.44
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.6
0
Iron (Fe), % 97.1 to 100
97.8 to 98.3
Manganese (Mn), % 0 to 1.5
1.4 to 1.7
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 0.55
0
Sulfur (S), % 0 to 0.045
0 to 0.050

Comparable Variants