EN 1.0038 Steel vs. Zamak 7

EN 1.0038 steel belongs to the iron alloys classification, while Zamak 7 belongs to the zinc alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0038 steel and the bottom bar is Zamak 7.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110 to 120
80
Elastic (Young's, Tensile) Modulus, GPa 190
86
Elongation at Break, % 23 to 25
13
Fatigue Strength, MPa 140 to 160
47
Poisson's Ratio 0.29
0.25
Shear Modulus, GPa 73
33
Shear Strength, MPa 240 to 270
210
Tensile Strength: Ultimate (UTS), MPa 380 to 430
280
Tensile Strength: Yield (Proof), MPa 200 to 220
250

Thermal Properties

Latent Heat of Fusion, J/g 250
120
Maximum Temperature: Mechanical, °C 400
95
Melting Completion (Liquidus), °C 1460
390
Melting Onset (Solidus), °C 1420
380
Specific Heat Capacity, J/kg-K 470
410
Thermal Conductivity, W/m-K 49
110
Thermal Expansion, µm/m-K 12
27

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
27
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
38

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
11
Density, g/cm3 7.8
6.4
Embodied Carbon, kg CO2/kg material 1.4
3.0
Embodied Energy, MJ/kg 19
57
Embodied Water, L/kg 48
380

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72 to 88
36
Resilience: Unit (Modulus of Resilience), kJ/m3 110 to 130
370
Stiffness to Weight: Axial, points 13
7.5
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 13 to 15
12
Strength to Weight: Bending, points 15 to 16
15
Thermal Diffusivity, mm2/s 13
43
Thermal Shock Resistance, points 12 to 13
8.6

Alloy Composition

Aluminum (Al), % 0
3.5 to 4.3
Cadmium (Cd), % 0
0 to 0.0020
Carbon (C), % 0 to 0.23
0
Chromium (Cr), % 0 to 0.3
0
Copper (Cu), % 0 to 0.6
0 to 0.25
Iron (Fe), % 97.1 to 100
0 to 0.075
Lead (Pb), % 0
0 to 0.0030
Magnesium (Mg), % 0
0.0050 to 0.020
Manganese (Mn), % 0 to 1.5
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0.0050 to 0.020
Nitrogen (N), % 0 to 0.014
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 0.55
0
Sulfur (S), % 0 to 0.045
0
Tin (Sn), % 0
0 to 0.0010
Zinc (Zn), % 0
95.3 to 96.5