EN 1.0116 Steel vs. AISI 317LN Stainless Steel

Both EN 1.0116 steel and AISI 317LN stainless steel are iron alloys. They have 64% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0116 steel and the bottom bar is AISI 317LN stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
45
Fatigue Strength, MPa 140
250
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
79
Shear Strength, MPa 240
430
Tensile Strength: Ultimate (UTS), MPa 380
620
Tensile Strength: Yield (Proof), MPa 200
270

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
1010
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
14
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
2.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
21
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
4.3
Embodied Energy, MJ/kg 19
59
Embodied Water, L/kg 47
160

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72
220
Resilience: Unit (Modulus of Resilience), kJ/m3 110
190
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 13
22
Strength to Weight: Bending, points 15
20
Thermal Diffusivity, mm2/s 13
3.9
Thermal Shock Resistance, points 12
14

Alloy Composition

Carbon (C), % 0 to 0.17
0 to 0.030
Chromium (Cr), % 0 to 0.3
18 to 20
Iron (Fe), % 97.1 to 100
57.9 to 67.9
Manganese (Mn), % 0 to 1.4
0 to 2.0
Molybdenum (Mo), % 0 to 0.080
3.0 to 4.0
Nickel (Ni), % 0 to 0.3
11 to 15
Nitrogen (N), % 0
0.1 to 0.22
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.55
0 to 0.75
Sulfur (S), % 0 to 0.035
0 to 0.030