EN 1.0116 Steel vs. EN 1.8831 Steel

Both EN 1.0116 steel and EN 1.8831 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0116 steel and the bottom bar is EN 1.8831 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
19
Fatigue Strength, MPa 140
330
Impact Strength: V-Notched Charpy, J 28
110
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 240
390
Tensile Strength: Ultimate (UTS), MPa 380
630
Tensile Strength: Yield (Proof), MPa 200
480

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
49
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.6
Embodied Energy, MJ/kg 19
21
Embodied Water, L/kg 47
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72
110
Resilience: Unit (Modulus of Resilience), kJ/m3 110
620
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13
22
Strength to Weight: Bending, points 15
21
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 12
18

Alloy Composition

Aluminum (Al), % 0
0.020 to 0.040
Carbon (C), % 0 to 0.17
0 to 0.16
Chromium (Cr), % 0 to 0.3
0
Iron (Fe), % 97.1 to 100
96.6 to 99.98
Manganese (Mn), % 0 to 1.4
0 to 1.7
Molybdenum (Mo), % 0 to 0.080
0 to 0.2
Nickel (Ni), % 0 to 0.3
0 to 0.5
Niobium (Nb), % 0
0 to 0.050
Nitrogen (N), % 0
0 to 0.020
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 0.55
0 to 0.6
Sulfur (S), % 0 to 0.035
0 to 0.0050
Titanium (Ti), % 0
0 to 0.050
Vanadium (V), % 0
0 to 0.1