EN 1.0116 Steel vs. SAE-AISI 1117 Steel

Both EN 1.0116 steel and SAE-AISI 1117 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0116 steel and the bottom bar is SAE-AISI 1117 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
140 to 150
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
17 to 26
Fatigue Strength, MPa 140
190 to 300
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 240
320 to 330
Tensile Strength: Ultimate (UTS), MPa 380
490 to 540
Tensile Strength: Yield (Proof), MPa 200
260 to 460

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
52
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
1.8
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
18
Embodied Water, L/kg 47
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72
86 to 110
Resilience: Unit (Modulus of Resilience), kJ/m3 110
180 to 550
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13
17 to 19
Strength to Weight: Bending, points 15
18 to 19
Thermal Diffusivity, mm2/s 13
14
Thermal Shock Resistance, points 12
15 to 17

Alloy Composition

Carbon (C), % 0 to 0.17
0.14 to 0.2
Chromium (Cr), % 0 to 0.3
0
Iron (Fe), % 97.1 to 100
98.3 to 98.8
Manganese (Mn), % 0 to 1.4
1.0 to 1.3
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.55
0
Sulfur (S), % 0 to 0.035
0.080 to 0.13