EN 1.0116 Steel vs. SAE-AISI 4047 Steel

Both EN 1.0116 steel and SAE-AISI 4047 steel are iron alloys. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0116 steel and the bottom bar is SAE-AISI 4047 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
170
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
23
Fatigue Strength, MPa 140
220
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 240
370
Tensile Strength: Ultimate (UTS), MPa 380
580
Tensile Strength: Yield (Proof), MPa 200
310

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
48
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72
110
Resilience: Unit (Modulus of Resilience), kJ/m3 110
260
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13
20
Strength to Weight: Bending, points 15
20
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 12
18

Alloy Composition

Carbon (C), % 0 to 0.17
0.45 to 0.5
Chromium (Cr), % 0 to 0.3
0
Iron (Fe), % 97.1 to 100
97.9 to 98.5
Manganese (Mn), % 0 to 1.4
0.7 to 0.9
Molybdenum (Mo), % 0 to 0.080
0.2 to 0.3
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 0.55
0.15 to 0.35
Sulfur (S), % 0 to 0.035
0 to 0.040