EN 1.0116 Steel vs. SAE-AISI 4145 Steel

Both EN 1.0116 steel and SAE-AISI 4145 steel are iron alloys. They have a very high 98% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.0116 steel and the bottom bar is SAE-AISI 4145 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 110
310
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
16
Fatigue Strength, MPa 140
240
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 240
360
Tensile Strength: Ultimate (UTS), MPa 380
580
Tensile Strength: Yield (Proof), MPa 200
360

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
420
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
42
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
2.4
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.5
Embodied Energy, MJ/kg 19
20
Embodied Water, L/kg 47
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72
80
Resilience: Unit (Modulus of Resilience), kJ/m3 110
350
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13
21
Strength to Weight: Bending, points 15
20
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 12
17

Alloy Composition

Carbon (C), % 0 to 0.17
0.43 to 0.48
Chromium (Cr), % 0 to 0.3
0.8 to 1.1
Iron (Fe), % 97.1 to 100
96.7 to 97.7
Manganese (Mn), % 0 to 1.4
0.75 to 1.0
Molybdenum (Mo), % 0 to 0.080
0.15 to 0.25
Nickel (Ni), % 0 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 0.55
0.15 to 0.35
Sulfur (S), % 0 to 0.035
0 to 0.040