EN 1.0116 Steel vs. SAE-AISI P21 Steel

Both EN 1.0116 steel and SAE-AISI P21 steel are iron alloys. They have a moderately high 94% of their average alloy composition in common. There are 23 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.0116 steel and the bottom bar is SAE-AISI P21 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 380
1130

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
41
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
6.5
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.4
2.3
Embodied Energy, MJ/kg 19
32
Embodied Water, L/kg 47
62

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13
40
Strength to Weight: Bending, points 15
31
Thermal Diffusivity, mm2/s 13
11
Thermal Shock Resistance, points 12
37

Alloy Composition

Carbon (C), % 0 to 0.17
0.18 to 0.22
Chromium (Cr), % 0 to 0.3
0 to 0.5
Cobalt (Co), % 0
1.1 to 1.3
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 97.1 to 100
92.1 to 94.2
Manganese (Mn), % 0 to 1.4
0.35 to 0.72
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
3.9 to 4.3
Phosphorus (P), % 0 to 0.035
0 to 0.030
Silicon (Si), % 0 to 0.55
0.2 to 0.4
Sulfur (S), % 0 to 0.035
0 to 0.030
Vanadium (V), % 0
0.15 to 0.25