EN 1.0116 Steel vs. N08811 Stainless Steel

Both EN 1.0116 steel and N08811 stainless steel are iron alloys. They have 46% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.0116 steel and the bottom bar is N08811 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
33
Fatigue Strength, MPa 140
150
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
77
Shear Strength, MPa 240
340
Tensile Strength: Ultimate (UTS), MPa 380
510
Tensile Strength: Yield (Proof), MPa 200
190

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1390
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
12
Thermal Expansion, µm/m-K 12
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.0
30
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.4
5.3
Embodied Energy, MJ/kg 19
76
Embodied Water, L/kg 47
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 72
130
Resilience: Unit (Modulus of Resilience), kJ/m3 110
94
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 13
18
Strength to Weight: Bending, points 15
18
Thermal Diffusivity, mm2/s 13
3.0
Thermal Shock Resistance, points 12
13

Alloy Composition

Aluminum (Al), % 0
0.15 to 0.6
Carbon (C), % 0 to 0.17
0.060 to 0.1
Chromium (Cr), % 0 to 0.3
19 to 23
Copper (Cu), % 0
0 to 0.75
Iron (Fe), % 97.1 to 100
39.5 to 50.6
Manganese (Mn), % 0 to 1.4
0 to 1.5
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
30 to 35
Phosphorus (P), % 0 to 0.035
0 to 0.040
Silicon (Si), % 0 to 0.55
0 to 1.0
Sulfur (S), % 0 to 0.035
0 to 0.015
Titanium (Ti), % 0
0.15 to 0.6