EN 1.0258 Steel vs. EN 1.0540 Steel

Both EN 1.0258 steel and EN 1.0540 steel are iron alloys. Both are furnished in the normalized condition. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0258 steel and the bottom bar is EN 1.0540 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
14
Fatigue Strength, MPa 200
210
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
72
Shear Strength, MPa 310
400
Tensile Strength: Ultimate (UTS), MPa 490
660
Tensile Strength: Yield (Proof), MPa 290
330

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
48
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.1
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 1.5
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
75
Resilience: Unit (Modulus of Resilience), kJ/m3 220
290
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
23
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 16
21

Alloy Composition

Carbon (C), % 0 to 0.2
0.47 to 0.55
Chromium (Cr), % 0 to 0.3
0 to 0.4
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.9 to 100
97.2 to 98.9
Manganese (Mn), % 0 to 1.4
0.6 to 0.9
Molybdenum (Mo), % 0 to 0.080
0 to 0.1
Nickel (Ni), % 0 to 0.3
0 to 0.4
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 0.4
Sulfur (S), % 0 to 0.020
0 to 0.045
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0