EN 1.0259 Steel vs. EN 1.4580 Stainless Steel

Both EN 1.0259 steel and EN 1.4580 stainless steel are iron alloys. They have 68% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.0259 steel and the bottom bar is EN 1.4580 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
200
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
40
Fatigue Strength, MPa 200
210
Impact Strength: V-Notched Charpy, J 38
90
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 310
430
Tensile Strength: Ultimate (UTS), MPa 490
620
Tensile Strength: Yield (Proof), MPa 280
250

Thermal Properties

Latent Heat of Fusion, J/g 250
290
Maximum Temperature: Mechanical, °C 400
950
Melting Completion (Liquidus), °C 1460
1450
Melting Onset (Solidus), °C 1420
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
15
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
22
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
4.3
Embodied Energy, MJ/kg 19
60
Embodied Water, L/kg 49
150

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
200
Resilience: Unit (Modulus of Resilience), kJ/m3 210
150
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
25
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 13
4.0
Thermal Shock Resistance, points 15
14

Alloy Composition

Aluminum (Al), % 0.020 to 0.2
0
Carbon (C), % 0 to 0.2
0 to 0.080
Chromium (Cr), % 0 to 0.3
16.5 to 18.5
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.7 to 99.98
61.4 to 71
Manganese (Mn), % 0 to 1.4
0 to 2.0
Molybdenum (Mo), % 0 to 0.080
2.0 to 2.5
Nickel (Ni), % 0 to 0.3
10.5 to 13.5
Niobium (Nb), % 0 to 0.010
0 to 1.0
Phosphorus (P), % 0 to 0.025
0 to 0.045
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0