EN 1.0259 (P265TR2) Non-Alloy Steel

EN 1.0259 steel is a carbon (non-alloy) steel formulated for primary forming into wrought products. Cited properties are appropriate for the normalized condition. 1.0259 is the EN numeric designation for this material. P265TR2 is the EN chemical designation.

It has a moderately high electrical conductivity and a moderately low thermal conductivity among wrought carbon or non-alloy steels.

The graph bars on the material properties cards below compare EN 1.0259 steel to: wrought carbon or non-alloy steels (top), all iron alloys (middle), and the entire database (bottom). A full bar means this is the highest value in the relevant set. A half-full bar means it's 50% of the highest, and so on.

Mechanical Properties

Brinell Hardness

140

Elastic (Young's, Tensile) Modulus

190 GPa 27 x 106 psi

Elongation at Break

23 %

Fatigue Strength

200 MPa 29 x 103 psi

Impact Strength: V-Notched Charpy

38 J 28 ft-lb

Poisson's Ratio

0.29

Shear Modulus

73 GPa 11 x 106 psi

Shear Strength

310 MPa 45 x 103 psi

Tensile Strength: Ultimate (UTS)

490 MPa 71 x 103 psi

Tensile Strength: Yield (Proof)

280 MPa 41 x 103 psi

Thermal Properties

Latent Heat of Fusion

250 J/g

Maximum Temperature: Mechanical

400 °C 750 °F

Melting Completion (Liquidus)

1460 °C 2660 °F

Melting Onset (Solidus)

1420 °C 2590 °F

Specific Heat Capacity

470 J/kg-K 0.11 BTU/lb-°F

Thermal Conductivity

49 W/m-K 28 BTU/h-ft-°F

Thermal Expansion

12 µm/m-K

Electrical Properties

Electrical Conductivity: Equal Volume

7.3 % IACS

Electrical Conductivity: Equal Weight (Specific)

8.4 % IACS

Otherwise Unclassified Properties

Base Metal Price

2.1 % relative

Density

7.8 g/cm3 490 lb/ft3

Embodied Carbon

1.5 kg CO2/kg material

Embodied Energy

19 MJ/kg 8.4 x 103 BTU/lb

Embodied Water

49 L/kg 5.8 gal/lb

Common Calculations

Resilience: Ultimate (Unit Rupture Work)

95 MJ/m3

Resilience: Unit (Modulus of Resilience)

210 kJ/m3

Stiffness to Weight: Axial

13 points

Stiffness to Weight: Bending

24 points

Strength to Weight: Axial

17 points

Strength to Weight: Bending

18 points

Thermal Diffusivity

13 mm2/s

Thermal Shock Resistance

15 points

Alloy Composition

Iron (Fe) 96.7 to 99.98
Manganese (Mn) 0 to 1.4
Silicon (Si) 0 to 0.4
Chromium (Cr) 0 to 0.3
Nickel (Ni) 0 to 0.3
Copper (Cu) 0 to 0.3
Aluminum (Al) 0.020 to 0.2
Carbon (C) 0 to 0.2
Molybdenum (Mo) 0 to 0.080
Titanium (Ti) 0 to 0.040
Phosphorus (P) 0 to 0.025
Vanadium (V) 0 to 0.020
Sulfur (S) 0 to 0.015
Niobium (Nb) 0 to 0.010

All values are % weight. Ranges represent what is permitted under applicable standards.

Followup Questions

Similar Alloys

Further Reading

EN 10216-1: Seamless steel tubes for pressure purposes - Technical delivery conditions - Part 1: Non-alloy steel tubes with specified room temperature properties

EN 10217-1: Welded steel tubes for pressure purposes - Technical delivery conditions - Part 1: Non-alloy steel tubes with specified room temperature properties

Microstructure of Steels and Cast Irons, Madeleine Durand-Charre, 2004

Carbon Steel Handbook, D. Gandy, 2007

Ferrous Materials: Steel and Cast Iron, Hans Berns and Werner Theisen, 2008

CRC Materials Science and Engineering Handbook, 4th ed., James F. Shackelford et al. (editors), 2015

Steels: Processing, Structure, and Performance, 2nd ed., George Krauss, 2015