EN 1.0259 Steel vs. EN 1.8872 Steel

Both EN 1.0259 steel and EN 1.8872 steel are iron alloys. Their average alloy composition is basically identical.

For each property being compared, the top bar is EN 1.0259 steel and the bottom bar is EN 1.8872 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 23
21
Fatigue Strength, MPa 200
310
Impact Strength: V-Notched Charpy, J 38
90
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 310
380
Tensile Strength: Ultimate (UTS), MPa 490
610
Tensile Strength: Yield (Proof), MPa 280
450

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
410
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
39
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.8
Density, g/cm3 7.8
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.7
Embodied Energy, MJ/kg 19
22
Embodied Water, L/kg 49
50

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
120
Resilience: Unit (Modulus of Resilience), kJ/m3 210
530
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 13
10
Thermal Shock Resistance, points 15
18

Alloy Composition

Aluminum (Al), % 0.020 to 0.2
0
Boron (B), % 0
0 to 0.0050
Carbon (C), % 0 to 0.2
0 to 0.18
Chromium (Cr), % 0 to 0.3
0 to 0.5
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 96.7 to 99.98
95.1 to 100
Manganese (Mn), % 0 to 1.4
0 to 1.7
Molybdenum (Mo), % 0 to 0.080
0 to 0.5
Nickel (Ni), % 0 to 0.3
0 to 1.0
Niobium (Nb), % 0 to 0.010
0 to 0.050
Nitrogen (N), % 0
0 to 0.015
Phosphorus (P), % 0 to 0.025
0 to 0.020
Silicon (Si), % 0 to 0.4
0 to 0.5
Sulfur (S), % 0 to 0.015
0 to 0.0080
Titanium (Ti), % 0 to 0.040
0 to 0.030
Vanadium (V), % 0 to 0.020
0 to 0.080
Zirconium (Zr), % 0
0 to 0.050