EN 1.0259 Steel vs. N08320 Stainless Steel

Both EN 1.0259 steel and N08320 stainless steel are iron alloys. They have 46% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.0259 steel and the bottom bar is N08320 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
190
Elastic (Young's, Tensile) Modulus, GPa 190
200
Elongation at Break, % 23
40
Fatigue Strength, MPa 200
190
Poisson's Ratio 0.29
0.28
Shear Modulus, GPa 73
78
Shear Strength, MPa 310
400
Tensile Strength: Ultimate (UTS), MPa 490
580
Tensile Strength: Yield (Proof), MPa 280
220

Thermal Properties

Latent Heat of Fusion, J/g 250
300
Maximum Temperature: Mechanical, °C 400
1100
Melting Completion (Liquidus), °C 1460
1400
Melting Onset (Solidus), °C 1420
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 49
12
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 8.4
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
28
Density, g/cm3 7.8
8.0
Embodied Carbon, kg CO2/kg material 1.5
4.9
Embodied Energy, MJ/kg 19
69
Embodied Water, L/kg 49
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95
180
Resilience: Unit (Modulus of Resilience), kJ/m3 210
120
Stiffness to Weight: Axial, points 13
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 17
20
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 13
3.3
Thermal Shock Resistance, points 15
13

Alloy Composition

Aluminum (Al), % 0.020 to 0.2
0
Carbon (C), % 0 to 0.2
0 to 0.050
Chromium (Cr), % 0 to 0.3
21 to 23
Copper (Cu), % 0 to 0.3
0
Iron (Fe), % 96.7 to 99.98
40.4 to 50
Manganese (Mn), % 0 to 1.4
0 to 2.5
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
25 to 27
Niobium (Nb), % 0 to 0.010
0
Phosphorus (P), % 0 to 0.025
0 to 0.040
Silicon (Si), % 0 to 0.4
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0