EN 1.0314 Steel vs. ASTM A210 Steel

Both EN 1.0314 steel and ASTM A210 steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0314 steel and the bottom bar is ASTM A210 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 92 to 120
140 to 160
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 24 to 25
34
Fatigue Strength, MPa 140 to 220
230 to 250
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 200 to 250
320 to 360
Tensile Strength: Ultimate (UTS), MPa 320 to 400
470 to 540
Tensile Strength: Yield (Proof), MPa 190 to 310
290 to 310

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1470
1460 to 1470
Melting Onset (Solidus), °C 1430
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 53
52 to 53
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 6.9
7.0
Electrical Conductivity: Equal Weight (Specific), % IACS 7.9
8.0 to 8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 1.8
1.8
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 18
18
Embodied Water, L/kg 46
45 to 46

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 68 to 87
140 to 160
Resilience: Unit (Modulus of Resilience), kJ/m3 95 to 250
230 to 250
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 11 to 14
17 to 19
Strength to Weight: Bending, points 13 to 15
17 to 19
Thermal Diffusivity, mm2/s 14
14
Thermal Shock Resistance, points 10 to 13
15 to 17