EN 1.0345 Steel vs. R60704 Alloy

EN 1.0345 steel belongs to the iron alloys classification, while R60704 alloy belongs to the otherwise unclassified metals. There are 20 material properties with values for both materials. Properties with values for just one material (12, in this case) are not shown.

For each property being compared, the top bar is EN 1.0345 steel and the bottom bar is R60704 alloy.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
97
Elongation at Break, % 27
16
Poisson's Ratio 0.29
0.34
Shear Modulus, GPa 73
36
Tensile Strength: Ultimate (UTS), MPa 420
470
Tensile Strength: Yield (Proof), MPa 230
270

Thermal Properties

Latent Heat of Fusion, J/g 250
240
Specific Heat Capacity, J/kg-K 470
270
Thermal Conductivity, W/m-K 49
22
Thermal Expansion, µm/m-K 12
6.0

Otherwise Unclassified Properties

Density, g/cm3 7.9
6.7
Embodied Water, L/kg 48
460

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 96
64
Resilience: Unit (Modulus of Resilience), kJ/m3 140
370
Stiffness to Weight: Axial, points 13
8.1
Stiffness to Weight: Bending, points 24
23
Strength to Weight: Axial, points 15
20
Strength to Weight: Bending, points 16
20
Thermal Diffusivity, mm2/s 13
12
Thermal Shock Resistance, points 13
58

Alloy Composition

Aluminum (Al), % 0.020 to 0.024
0
Carbon (C), % 0 to 0.16
0 to 0.050
Chromium (Cr), % 0 to 0.3
0.2 to 0.4
Copper (Cu), % 0 to 0.3
0
Hafnium (Hf), % 0
0 to 4.5
Hydrogen (H), % 0
0 to 0.0050
Iron (Fe), % 97.2 to 99.38
0.2 to 0.4
Manganese (Mn), % 0.6 to 1.2
0
Molybdenum (Mo), % 0 to 0.080
0
Nickel (Ni), % 0 to 0.3
0
Niobium (Nb), % 0 to 0.020
0
Nitrogen (N), % 0 to 0.012
0 to 0.025
Oxygen (O), % 0
0 to 0.18
Phosphorus (P), % 0 to 0.025
0
Silicon (Si), % 0 to 0.35
0
Sulfur (S), % 0 to 0.010
0
Tin (Sn), % 0
1.0 to 2.0
Titanium (Ti), % 0 to 0.030
0
Vanadium (V), % 0 to 0.020
0
Zirconium (Zr), % 0
93 to 98.8