MakeItFrom.com
Menu (ESC)

EN 1.0402 Steel vs. EN 1.0116 Steel

Both EN 1.0402 steel and EN 1.0116 steel are iron alloys. Both are furnished in the normalized condition. Their average alloy composition is basically identical. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.0402 steel and the bottom bar is EN 1.0116 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 130
110
Elastic (Young's, Tensile) Modulus, GPa 190
190
Elongation at Break, % 24
23
Fatigue Strength, MPa 170
140
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Shear Strength, MPa 290
240
Tensile Strength: Ultimate (UTS), MPa 460
380
Tensile Strength: Yield (Proof), MPa 240
200

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
400
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 50
49
Thermal Expansion, µm/m-K 12
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.1
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 8.2
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
2.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 1.4
1.4
Embodied Energy, MJ/kg 19
19
Embodied Water, L/kg 47
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 94
72
Resilience: Unit (Modulus of Resilience), kJ/m3 150
110
Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 16
13
Strength to Weight: Bending, points 17
15
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 15
12

Alloy Composition

Carbon (C), % 0.17 to 0.24
0 to 0.17
Chromium (Cr), % 0 to 0.4
0 to 0.3
Iron (Fe), % 97.7 to 99.43
97.1 to 100
Manganese (Mn), % 0.4 to 0.7
0 to 1.4
Molybdenum (Mo), % 0 to 0.1
0 to 0.080
Nickel (Ni), % 0 to 0.4
0 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.035
Silicon (Si), % 0 to 0.4
0 to 0.55
Sulfur (S), % 0 to 0.045
0 to 0.035