EN 1.0451 Steel vs. EN 1.3533 Steel

Both EN 1.0451 steel and EN 1.3533 steel are iron alloys. They have a very high 95% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.0451 steel and the bottom bar is EN 1.3533 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 120
210 to 220
Elastic (Young's, Tensile) Modulus, GPa 190
190
Poisson's Ratio 0.29
0.29
Shear Modulus, GPa 73
73
Tensile Strength: Ultimate (UTS), MPa 420
690 to 1420

Thermal Properties

Latent Heat of Fusion, J/g 250
250
Maximum Temperature: Mechanical, °C 400
440
Melting Completion (Liquidus), °C 1460
1460
Melting Onset (Solidus), °C 1420
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 49
47
Thermal Expansion, µm/m-K 12
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 7.2
7.9
Electrical Conductivity: Equal Weight (Specific), % IACS 8.3
9.0

Otherwise Unclassified Properties

Base Metal Price, % relative 2.1
5.0
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 1.5
1.8
Embodied Energy, MJ/kg 19
25
Embodied Water, L/kg 48
60

Common Calculations

Stiffness to Weight: Axial, points 13
13
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 15
24 to 50
Strength to Weight: Bending, points 16
22 to 36
Thermal Diffusivity, mm2/s 13
13
Thermal Shock Resistance, points 13
20 to 42

Alloy Composition

Aluminum (Al), % 0.020 to 0.060
0 to 0.050
Carbon (C), % 0 to 0.15
0.15 to 0.2
Chromium (Cr), % 0 to 0.3
1.3 to 1.6
Copper (Cu), % 0 to 0.3
0 to 0.3
Iron (Fe), % 97.2 to 99.58
92.9 to 94.9
Manganese (Mn), % 0.4 to 1.2
0.4 to 0.7
Molybdenum (Mo), % 0 to 0.080
0.15 to 0.25
Nickel (Ni), % 0 to 0.3
3.3 to 3.8
Niobium (Nb), % 0 to 0.010
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.35
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.030
Titanium (Ti), % 0 to 0.040
0
Vanadium (V), % 0 to 0.020
0